Advanced Composites ATX913-2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Advanced Composites, Inc. |
| Trademark: | Advanced Composites |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 510GYY_Advanced-Composites-ATX913-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Advanced Composites ATX913-2 is a polypropylene product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.2 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 24.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 130 | % | ASTM D638 |
| Flexural Modulus 3 | 2220 | MPa | ASTM D790 |
| Flexural Strength 4 | 39.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 127 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Cushion | 10.0 - 20.0 | mm |
| Injection instructions |
|---|
| Injection Pressure: 50 to60% of amchine capacityScrew RPM: 1 to 2 secs before mold open |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP521-231UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| ANYPOL CL-3000F | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Forprene® 6NE901A45 | SO.F.TER. SPA | TPV | Forprene® |
| Hifax ETA3104HF | LyondellBasell Industries | TPO (POE) | Hifax |
| ESPRENE EPDM 601F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |