Tenopom® POM B3 HF NTLA010 PR306
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Tenopom® POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4zVggV_Tenopom-POM-B3-HF-NTLA010-PR306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyacetal copolymer with low viscosity in natural color, easy processing, suitable for injection parts where it needs to be easily completed. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 24 to 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 61.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 46 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 100 | °C | |
| Melting Temperature | 170 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dissipation Factor (1 MHz) | 6.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BW1XBK6468 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| TRIREX® Compound 3025AS | Samyang Corporation | PC | TRIREX® Compound |
| Geon™ Vinyl Flexible B8000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Huafon JF-P-8465 / JF-I-4419 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| LNP™ THERMOCOMP™ UFW49S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |