TEKASTER™ F615G30
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKASTER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4xkK6Y_TEKASTER-F615G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| F615G30 is GF 30% reinforced polyethylene terephthalate (PET). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 152 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.7 | % | ASTM D638 |
| Flexural Modulus 3 | 8730 | MPa | ASTM D790 |
| Flexural Strength 4 | 230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 99 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 247 | °C | |
| 1.8 MPa, Unannealed | 225 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 245 to 255 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 255 to 265 | °C | |
| Nozzle Temperature | 255 to 265 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell PP EA-14 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| DIALAC® S359E | UMG ABS, Ltd. | ASA+PMMA | DIALAC® |
| FHR Polypropylene P6G4Z-097 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Polifor® C 30 TE/40 BIANCO 0330 | SO.F.TER. SPA | PP Copolymer | Polifor® |
| Sylvin 6242-70LG Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |