DOWLEX™ SC 2107GS
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4xDdC4_DOWLEX-SC-2107GS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ SC 2107GS is ultra low gel ethylene octene copolymer. Films made from DOWLEX SC 2107GS Polyethylene Resin is processable at high line speeds, exhibits excellent stretchability, outstanding tear and impact resistance, as well as exceptional optical properties. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 23 µm | 6.30 | MPa | ASTM D882 |
| TD : Yield, 23 µm | 5.90 | MPa | ASTM D882 |
| MD : Break, 23 µm | 43.0 | MPa | ASTM D882 |
| TD : Break, 23 µm | 28.0 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Break, 23 µm | 470 | % | ASTM D882 |
| TD : Break, 23 µm | 900 | % | ASTM D882 |
| Dart Drop Impact 3(23 µm) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 23 µm | 410 | g | ASTM D1922 |
| TD : 23 µm | 540 | g | ASTM D1922 |
| Film tensile properties-maximum stretch to penetration 5 | 130 | Internal method | |
| Film Tensile Properties-Maximum Elongation 6 | 240 | % | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 7(45°, 23.0 µm) | 92 | ASTM D2457 | |
| Haze 8(23.0 µm) | 0.70 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 熔体温度：220-280°C 冷却辊温度：20-60°C 脱离速度：150-450 米/分 建议的厚度范围：10-60 µm |
| Note Message | |
|---|---|
| 1 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 2 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 3 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 4 . | Method B; Cast film, 250 m/min; Cooling roller 25 c. |
| 5 . | Cast film, 250 m/min; Cooling roller 25°C; Measured on test bench; Maximum prestretching before penetration of sharp probe. |
| 6 . | Cast film, 250 m/min, cooling roller 25°C; Measured on the test bench. |
| 7 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 8 . | Cast film, 250 m/min; Cooling roller 25 c. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3703 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Spartech Polycom SC21-1091 | Spartech Polycom | PBT | Spartech |
| Elastocon® 8058BL | Elastocon TPE Technologies | TPE | Elastocon® |
| Hypro® PP-CP 8/6 | Entec Polymers | PP Impact Copolymer | Hypro® |
| ULTEM™ 1010 resin | SABIC Innovative Plastics | PEI | ULTEM™ |