SCHULAMID® 66 CF 20 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4wgeBF_SCHULAMID-66-CF-20-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% carbon fiber reinforced, heat stabilized Polyamide 66 with very high tensile strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.21 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 300 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17000 | 11000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 220 | 160 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | 5.2 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 13000 | -- | MPa | ISO 178 |
| Flexural Stress | 315 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 3.6 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 8.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | -- | kJ/m² | |
| 23°C | 60 | 85 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 246 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | > 250 | -- | °C | ISO 306/A50, ISO 306/B50 |
| Ball Pressure Test (220°C) | Pass | -- | IEC 60695-10-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+4 | > 1.0E+6 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+3 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 100 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® RP 2001-C | Plastic Solutions, Inc. | PP Random Copolymer | PrimaFlex® |
| Small Boss SPVC005 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Flexible | Small Boss |
| Hostalen PP H2142 12 | LyondellBasell Industries | PP Impact Copolymer | Hostalen PP |
| INLUBE PA6TF20 | Infinity LTL Engineered Compounds | Nylon 6 | INLUBE |
| LNP™ LUBRICOMP™ CBL36XXC compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ LUBRICOMP™ |