Hostaform® MT8F01
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4vQMGS_Hostaform-MT8F01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostaform® acetal copolymer grade MT8F01 is a special grade developed for medical industry applications containing low residual monomers. Hostaform® MT8F01 is a standard flow low level polytetrafluoroethylene filled (PTFE) product designed for use in wear applications against plastics, metal, glass or ceramic mating surfaces where silicone lubricants can not be tolerated. |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 28 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.2 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 176 | °C | |
| Middle Temperature | 182 | °C | |
| Front Temperature | 188 | °C | |
| Nozzle Temperature | 198 | °C | |
| Processing (Melt) Temp | 182 - 199 | °C | |
| Mold Temperature | 77.0 - 93.0 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 193°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Huafon JF-W-6110 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina NATURAL PVC COMPOUND -E V-150 LT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kepital® TE-23S | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Hostacom HYG 400-2 BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sylvin 7833-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |