QAMAR FC21HS
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SPDC Ltd. |
| Trademark: | QAMAR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4vGdsw_QAMAR-FC21HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
QAMAR FC21HS is a linear low density polyethylene material,. This product is available in North America, Africa and the Middle East, Europe or Asia Pacific region. The processing method is blow molded film. The main features of QAMAR FC21HS are:
The typical application fields of QAMAR FC21HS are: movies |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | JIS K6760 | ||
| Yield | 12.0 | MPa | JIS K6760 |
| Fracture | 32.0 | MPa | JIS K6760 |
| Tensile Strain (Break) | 900 | % | JIS K6760 |
| Apparent Bending Modulus | 260 | MPa | ASTM D747 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Modulus | ISO IR 1184 | ||
| MD : 30 µm | 190 | MPa | ISO IR 1184 |
| TD : 30 µm | 220 | MPa | ISO IR 1184 |
| Tensile Stress | JIS Z1702 | ||
| MD : Break, 30 µm | 55.0 | MPa | JIS Z1702 |
| TD : Break, 30 µm | 40.0 | MPa | JIS Z1702 |
| Tensile Elongation | JIS Z1702 | ||
| MD : Break, 30 µm | 550 | % | JIS Z1702 |
| TD : Break, 30 µm | 850 | % | JIS Z1702 |
| Dart Drop Impact (30 µm) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 30 | g | ASTM D1922 |
| TD : 30 µm | 160 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 9.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 210 | °C | |
| Melt Temperature (Aim) | 200 | °C |
| Extrusion instructions |
|---|
| Blow up Ratio: 2 to 4Screw Type: LLDPE ScrewDie Lip Gap: 2.0 to 3.0 mmAir Ring: Single or Dual Slit (Wide die) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil MED-4780 | NuSil Technology | Rubber | NuSil |
| ELASTOSIL® R 401/10 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Eltex® P KV409 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |
| G-Lex B52A003 | Gas Authority of India Limited | HDPE | G-Lex |
| POLYfill PPC T1020 | Polykemi AB | PP Copolymer | POLYfill |