Daicel PA PA9T-GF50-01
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Daicel PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4u3rpn_Daicel-PA-PA9T-GF50-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Daicel PA PA9T-GF50-01 is a Polyamide material filled with 50% long glass fiber. It is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.58 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Yield) | 245 | 220 | MPa | ISO 527-2 |
| Flexural Modulus | 16000 | 15500 | MPa | ISO 178 |
| Flexural Stress | 370 | 330 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 | 32 | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 295 | -- | °C | ISO 75-2/A |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 310 to 330 | °C | |
| Middle Temperature | 320 to 330 | °C | |
| Front Temperature | 320 to 330 | °C | |
| Nozzle Temperature | 310 to 330 | °C | |
| Mold Temperature | 130 to 150 | °C | |
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 GB 30 Z | RTP Company | PP Homopolymer | RTP |
| BAAF UHMW-PE M-0 | BAAF | HDPE, UHMW | BAAF UHMW-PE |
| Andur 7003 AP-M | Anderson Development Company | PUR-Ether/TDI | Andur |
| FORMULA P ELAN 3003 UV | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| LEXAN™ LS1 resin | SABIC Innovative Plastics | PC | LEXAN™ |