| Daicel PP PNAS3 is a Polypropylene material. It is available in Asia Pacific. Primary attribute of Daicel PP PNAS3: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.5 to 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 87 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 140 to 180 | °C | |
| Middle Temperature | 160 to 200 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 180 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 70 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 1000 RD01 | POLY GIN | PC | MARCOBLEND |
| TAIRIPRO K8025 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Lumid® SG2300B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |
| Sylvin 8784-77 Grey 9453 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ICORENE® 3940 | ICO Polymers NA, A Division of A. Schulman | LLDPE | ICORENE® |