Iupiace® AP4
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4tRyWG_Iupiace-AP4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupiace® AP4 is a Polyphenylene Ether + PS (PPE+PS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupiace® AP4 are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 70.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption (Saturation, 23°C) | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 49.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.2 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 45 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 250 to 280 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2100N0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TEKAMID™ TA210HI3 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Vyncolit® 1908K | Vyncolit N.V. | Epoxy | Vyncolit® |
| CP PRYME® Nylon 66 NN113L | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Formolene® L42022E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |