Plaslube® POM HO TL2
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4o8kh6_Plaslube-POM-HO-TL2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® POM HO TL2 is an Acetal (POM) Homopolymer product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.17 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 22 | % | ASTM D638 |
| Flexural Modulus | 2960 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.22 | ||
| vs. Steel - Static | 0.19 | ||
| Wear Factor | 100 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 166 | °C | |
| 1.8 MPa, Unannealed | 100 | °C | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 177 to 193 | °C | |
| Middle Temperature | 188 to 210 | °C | |
| Front Temperature | 182 to 199 | °C | |
| Nozzle Temperature | 177 to 204 | °C | |
| Processing (Melt) Temp | 193 to 216 | °C | |
| Mold Temperature | 82.2 to 121 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 70 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® GS6073 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Vydyne® R530H BK0201 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| 3M™ Dyneon™ PTFE TF 2029Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| ELASTOSIL® R 861/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| LNP™ THERMOCOMP™ RF008 compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |