TARODUR 150
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TARODUR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4nSHE7_TARODUR-150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ABS high impact strength, and good heat resistance. Approved FIAT SA 90.150 BL and ABS 95.150 Available: all colors, UV stabilized (L), heat stabilized (H) and antistatic (AS). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 to 0.70 | % | |
| Across Flow | 0.60 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 70.0 | MPa | ISO 178 |
| Yield | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 19 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 200 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 88.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ASTM D1525, ISO 306/A50 4 3 |
| -- | 92.0 | °C | ASTM D1525, ISO 306/B50 5 4 |
| Ball Pressure Test (75°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (2.00 mm) | 550 | °C | IEC 60695-2-13 |
| Oxygen Index | < 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 70.0 to 80.0 | °C | |
| Pre-heater | 70.0 to 80.0 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | 6x4x50 mm |
| 3 . | Rate A (50°C/h), Loading 1 (10 N) |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K8802 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Five Plus™ HPP30C | Noble Polymers | PP Homopolymer | Five Plus™ |
| En Chuan 6021H | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| IROSTIC® S 7514 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |
| OmniPro™ CPP CCF10 | OMNI Plastics, LLC | PP Copolymer | OmniPro™ |