Akulon® Ultraflow K-FKMV5
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® Ultraflow |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4mgg3Z_Akulon-Ultraflow-K-FKMV5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® Ultraflow K-FKMV5 is a Polyamide 6 (Nylon 6) material filled with 25% mineral. It is available in Asia Pacific or Europe. Important attributes of Akulon® Ultraflow K-FKMV5 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.60 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6200 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 65.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 2.0 | -- | kJ/m² | |
| 23°C | 2.0 | 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 25 | -- | kJ/m² | |
| 23°C | 25 | 30 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature (1.50 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 225 to 235 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 235 to 250 | °C | |
| Nozzle Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 235 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive SE900-6 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Syncure™ S1000B | PolyOne Corporation | XLPE | Syncure™ |
| Celanex® 6500HF | Celanese Corporation | PBT | Celanex® |
| Cheng Yu N6CV3 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| Karina PURPLE COLOR CONCENTRATE 52/ 10FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |