InnoPlus HD6000C
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4lSLWD_InnoPlus-HD6000C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus HD6000C and HD6001C are high density polyethylene with outstanding environmental stress cracking resistance (ESCR). Thanks to stress cracking resistance outperforming, these grades are suitable for beverage caps and closures for new caps design. They show good processability in either injection molding or compression molding machine. Additive InnoPlus HD6000C with slip agent. InnoPlus HD6001C without slip agent. Typical Application: Beverage caps for mineral, stilled, sparkling water and carbonated soft drink. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.957 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (25% Igepal, F50) | 390 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 31.4 | MPa | |
| Break | 38.2 | MPa | |
| Tensile Elongation (Break) | 1000 | % | ASTM D638 |
| Apparent Bending Modulus | 1080 | MPa | ASTM D747 |
| Flexural Modulus | 1370 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 2 |
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Temperature | 160 to 190 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | Partial Break |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Terblend® N NG-04 | INEOS Styrolution Group GmbH | ABS+Nylon | Terblend® N |
| Braskem PP HP 427J | Braskem | PP Homopolymer | Braskem PP |
| Formolene® 5140N | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| EPT 4021 | Mitsui Chemicals, Inc. | EPDM | EPT |
| Plexar® PX6005 | LyondellBasell Industries | PP, Unspecified | Plexar® |