CERTENE™ HMF-0856
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4lSDFh_CERTENE-HMF-0856.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HMF-0856 is a certified prime grade Hexene copolymer MEDIUM MOLECULAR WEIGHT developed for production of thin gauged high stiffness paper-like Blown films. HMF-0856 features BROAD molecular weight distribution for improved processability at lower extruder pressure, excellent film drawdown, and good combination of high film stiffness with good film strength and improved barrier properties. HMF-0856 can be easily processed in HMW high stalk film equipment or in conventional film lines equipped with die gap = 0.75 to 1.25 = mm.. HMF-0856 applications include deli, meat & cheese wrap films, cereal box liners, notion and millinery bags, small shoppers, multi-wall and single liners, lamination films, coextrusion of films for stand-up-still pouches, and as substitute films for grease-proof waxed and acid free papers. Minimum recommended film gauge is 12 microns (0.5 mil), and processing temperature 195° to 205° C. HMF-0856 complies with FDR regulation 21CFR 177.1520 (c) 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 31 | µm | |
| Film Thickness - Recommended / Available | Minimum 12 µm (0.5 mil) | ||
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 31 µm, blown film | 860 | MPa | ASTM D882 |
| 1% secant, TD : 31 µm, blown film | 1040 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 31 µm, blown film | 24.0 | MPa | ASTM D882 |
| TD : Yield, 31 µm, blown film | 14.0 | MPa | ASTM D882 |
| MD : Broken, 31 µm, blown film | 52.0 | MPa | ASTM D882 |
| TD : Broken, 31 µm, blown film | 19.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 31 µm, blown film | 570 | % | ASTM D882 |
| TD : Broken, 31 µm, blown film | 490 | % | ASTM D882 |
| Dart Drop Impact 1(31 µm, blown film) | 75 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 31 µm, blown film | 15 | g | ASTM D1922 |
| TD : 31 µm, blown film | 560 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 130 | °C | ASTM D3417 |
| Additional Information |
|---|
| Film Specimen: 1.25 mil (31 µm) film, melt temperature 410-440°F (210-225°C), blow-up-ratio 4.0:1, frost line height 8 x die ø. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 195 - 205 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESN P10 T | Arkema | Nylon 11 | Rilsan® |
| Ravago Compounds PP-3442 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| Sindustris ABS LHF491G | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| BLUESTAR庐 PBT 101G30 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| Polyrocks 666(f1) | Polyrocks Chemical Co., Ltd | PP, Unspecified | Polyrocks |