TROGAMID® CX CX7323
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | TROGAMID® CX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4k2oIm_TROGAMID-CX-CX7323.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
By selecting specific monomers, one can achieve a crystallizable and permanently transparent polyamide: TROGAMID® CX. The crystallites are so small that they do not scatter visible light, and the material appears transparent to the human eye—a property known as microcrystallinity. Because of its crystallinity, the microcrystalline structure retains important properties such as stress cracking resistance — without clouding. The degree of crystallinity is so negligible, however, that it has no adverse effect on the shrinkage behavior of molded parts. TROGAMID® CX undergoes a similar isotropic shrinkage like amorphous materials. The combination of good UV resistance, high mechanical strength, permanent transparency, high transmission and superior chemical resistance opens a wide range of applications for TROGAMID® CX. Typical areas of application are in the automotive industry, machinery and engineering, medical technology, the sports and recreation industry, the glasses production, the cosmetics industry and in water treatment and filter technology. TROGAMID® CX7323: Medium-viscous, permanently transparent polyamide for injection molding and extrusion |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.02 | g/cm³ | ISO 1183 |
| Viscosity Number | 150 to 170 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 | |
| Ball Indentation Hardness | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 1400 | MPa | |
| 80°C | 1270 | MPa | |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 60.0 | MPa | |
| Yield, 80°C | 48.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 8.0 | % | |
| Yield, 80°C | 5.5 | % | |
| Nominal Tensile Strain at Break | ISO 527-2/50 | ||
| 23°C | > 50 | % | |
| 80°C | > 50 | % | |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 1300 | MPa | |
| 1000 hr | 700 | MPa | |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Flexural Stress 1 | ISO 178 | ||
| 3.5% Strain | 50.0 | MPa | |
| -- | 90.0 | MPa | |
| Abrasion Resistance | 18.0 | mg/100 cycles | DIN 53754 |
| Outer Fiber Strain - at maximum stress 2 | 9.0 | % | ISO 178 |
| Scratch Resistance - % turbidity increase | 32.0 | DIN 52347 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Permeation | |||
| Carbon Dioxide : 20°C, 50.0 µm | 1.42E-8 | cm³·cm/cm²/sec/bar | |
| Nitrogen : 20°C, 50.0 µm | 5.00E-10 | cm³·cm/cm²/sec/bar | |
| Oxygen : 20°C, 50.0 µm | 4.30E-9 | cm³·cm/cm²/sec/bar |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Index 3 | 100 | °C | IEC 216 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dynamic Properties - Under load 4 | > 2.0E+5 | Cycles | DIN EN 13443-1 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Transmission Rate (20°C, 50 µm) | 2540 | cm³/m²/24 hr | |
| Nitrogen Transmission Rate (20°C, 50 µm) | 85.0 | cm³/m²/24 hr | |
| Oxygen Transmission Rate (20°C, 50 µm) | 740 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (23°C, 85% RH, 110 µm) | 8.3 | g/m²/24 hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 11 | kJ/m² | |
| 0°C, Complete Break | 12 | kJ/m² | |
| 23°C, Complete Break | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 0°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 108 | °C | ISO 75-2/A |
| Glass Transition Temperature 5 | 140 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ISO 306/A |
| -- | 130 | °C | ISO 306/B |
| Melting Temperature (DSC) 6 | 250 | °C | DSC |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 9.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.60 | ||
| 23°C, 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 0.012 | ||
| 23°C, 1 MHz | 0.033 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- 7 | 575 | V | |
| Solution A | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 800 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | Criterion: stress at yield |
| 4 . | Filter Cup |
| 5 . | 10 K/min |
| 6 . | 2nd Heating |
| 7 . | 100 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 303 UV | RTP Company | PC | RTP |
| Shuman PE 603 | Shuman Plastics, Inc. | PE, Unspecified | Shuman PE |
| Badadur® PBT8 TM-Z1 | Bada AG | PBT | Badadur® |
| Arnite® TV4 261 /A | DSM Engineering Plastics | PBT | Arnite® |
| SIBUR Synthetic Rubber NBR 1845 | SIBUR | NBR | SIBUR Synthetic Rubber |