Propafilm™ SNC25
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4ivd7n_Propafilm-SNC25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low Heat-Seal Threshold Film with Shrink Tightening Properties Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with heat-sealable polyolefinic copolymers. SNC25 is suitable for clear wrap/naked collation of wrapped packs where exceptional pack appearance is required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.25 | ||
| vs. Itself - Static, Outside/Outside | 0.30 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD : 25 µm | 3000 | MPa | |
| 1% Secant, TD : 25 µm | 3600 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 25 µm | 170 | MPa | |
| TD : Yield, 25 µm | 210 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break, 25 µm | 120 | % | |
| TD : Break, 25 µm | 80 | % | |
| Seal Strength 4 | 0.20 | N/mm | Internal Method |
| Seal Initiation Temperature | Internal Method | ||
| -- 5 | 100 to 120 | °C | |
| -- 6 | 100 to 140 | °C | |
| Water Vapor Transmission Rate | ASTM F1770 | ||
| 23°C, 85% RH, 25 µm | 1.0 | g/m²/24 hr | |
| 38°C, 90% RH, 25 µm | 5.0 | g/m²/24 hr |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 25.0 µm) | 125 | ASTM D2457 | |
| Haze 7(25.0 µm) | 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 109°C; 1sec; 0.10 MPa |
| 5 . | For Clear Wrap, 2secs; 0.10 MPa |
| 6 . | 2secs; 0.10 MPa |
| 7 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC EVA VS440 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| SHIN-A SE-55A | SHIN-A T&C | Epoxy | SHIN-A |
| SEPAZ™ LH40 | Mando Advanced Materials Co., Ltd. | PP Homopolymer | SEPAZ™ |
| DOW™ Electrical & Telecommunications DGDK-6862 NT | The Dow Chemical Company | HDPE | DOW™ Electrical & Telecommunications |
| NORYL GTX™ GTX989 resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |