VICTREX® PEEK 150GL15
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4iH9Ta_VICTREX-PEEK-150GL15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, 15% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food contact compliant, colour natural/beige. Complex geometries with thin cross sections or long flow lengths where good strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ISO 1183 |
| Spiral Flow | 18.0 | cm | Internal method |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Vertical flow direction : 180°C | 1.0 | % | ISO 294-4 |
| Flow direction : 180°C | 0.40 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.060 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 86 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.3 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 323 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | ISO 11357-2 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : > 143°C | 3.0E-4 | cm/cm/°C | ISO 11359-2 |
| Flow : < 143°C | 3.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 5.5E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 1.2E-3 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1700 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.30 | W/m/K | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 210 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 355 | °C | |
| Middle Temperature | 360 - 365 | °C | |
| Front Temperature | 370 | °C | |
| Nozzle Temperature | 375 | °C | |
| Mold Temperature | 170 - 200 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | Crystalline |
| 2 . | 375°C nozzle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® KN226 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| RTP 205 FR | RTP Company | Nylon 66 | RTP |
| VITAMIDE® BB74BG6579 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Ebalta AH 120 / TL | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Sylvin 8378-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |