Mold Max® 60
| Category: | Silicone , Silicone |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Mold Max® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4gG7Ma_Mold-Max-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mold Max® 60 is a Shore 60A tin catalyzed silicone rubber formulated for applications requiring high heat resistance (up to 560°F/294°C). It features a low mixed viscosity and cured rubber exhibits very low linear shrinkage. Parts A & B are mixed 100A & 3B by weight. Pot life is 40 minutes and cure time is 24 hours. Applications include making foundry patterns, flat pattern reproductions and casting low-melt metal alloys such as tin and pewter. PLEASE NOTE: THI-VEX® Silicone Thickener is NOT recommended for use with Mold Max® 60. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.690 | cm³/g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 100A:3B by weight | ||
| Operating Temperature | -54 to 293 | °C |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.15 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 2.28 | MPa | ASTM D412 |
| Tensile Strength (Break) | 2.74 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 130 | % | ASTM D412 |
| Tear Strength 1 | 11.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | 0.050 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 20 | kV/mm | ASTM D149 |
| Dielectric Constant (100 Hz) | 3.40 | ASTM D150 | |
| Dissipation Factor (100 Hz) | 0.020 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 40 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 20000 | cP | ASTM D2393 |
| Demold Time 2(23°C) | 1400 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| 2 . | Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Europrene Latice® B 010 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| KOPA® KN333HFBL1 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Karina YELLOW PVC COMPOUND 800-02/42-RTC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPC T4030 E20 | Polykemi AB | PP Copolymer | POLYfill |
| Sylvin 9777-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |