LNP™ LUBRICOMP™ YP003 compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4ddMFy_LNP-LUBRICOMP-YP003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* YP003 is a compound based on Polyester Elastomer resin containing 15% PTFE/Silicone. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound YL-4530 Product reorder name: YP003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 2.1 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 2.0 | % | ASTM D955 |
| Across Flow : 24 hr | 2.1 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.37 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 207 | MPa | ASTM D638 |
| -- | 240 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 13.9 | MPa | ASTM D638 |
| Yield | 14.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 54 | % | ASTM D638 |
| Yield | 40 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 262 | MPa | ASTM D790 |
| -- | 270 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.48 | ||
| vs. Itself - Static | 0.46 | ||
| Wear Factor - Washer | 5.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 240 | J/m | ASTM D256 |
| 23°C 2 | 27 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 27.7 | J | ASTM D3763 |
| -- | 26.9 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 47.2 | °C | ASTM D648 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.8E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 216 to 238 | °C | |
| Mold Temperature | 26.7 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V75T | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Tarnoform® 300 HI6 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Witcom HDPE 2007/492 | Witcom Engineering Plastics B.V. | HDPE | Witcom HDPE |
| Yuyao PET PETG20 (FR) | Yuyao Tenglong Plastics Co., Ltd. | PET | Yuyao PET |
| KOPLA PA66 KDP1000F | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |