Ketron® PEEK UHP320
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Ketron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4b3Y1a_Ketron-PEEK-UHP320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ketron® PEEK UHP320 is a Polyetheretherketone (PEEK) product. It can be processed by extrusion and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | |
| Saturation | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 100 | ||
| R-Scale | 126 | ||
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 172 | MPa | ASTM D790 |
| Compressive Modulus | 3450 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 138 | MPa | ASTM D695 |
| Shear Strength | 55.2 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.40 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 249 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.876 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 340 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 4 | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 3.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6710G | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Borlink™ LE0520 | Borealis AG | PE, Unspecified | Borlink™ |
| Geon™ Vinyl Wire & Cable WJJC310L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| LEXAN™ FXG154 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina BLACK PVC COMPOUND TR-55-48/1 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |