LNP™ LUBRICOMP™ UFL36S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4aBcx4_LNPLUBRICOMPUFL36Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* UFL36S is a compound based on Polyphthalamide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant, Bearing Grade. Also known as: LNP* LUBRICOMP* Compound BGU Product reorder name: UFL36S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.82 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.17 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.33 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12400 | MPa | ASTM D638 |
| -- | 9890 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 197 | MPa | ASTM D638 |
| Fracture | 196 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 10800 | MPa | ASTM D790 |
| -- | 11200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 281 | MPa | ASTM D790 |
| -- | 286 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.59 | ASTM D3702 Modified | |
| With Self-Static | 0.52 | ASTM D3702 Modified | |
| Wear Factor - Washer | 18.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 3 | 70 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.60 | J | ASTM D3763 |
| -- | 2.59 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 259 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 263 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 - 321 | °C | |
| Middle Temperature | 316 - 327 | °C | |
| Front Temperature | 327 - 338 | °C | |
| Processing (Melt) Temp | 316 - 332 | °C | |
| Mold Temperature | 149 - 171 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® ABS 1045 | Plastic Solutions, Inc. | ABS | PrimaFlex® |
| SABIC® PPcompound 2605 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| TOTAL Polyethylene Lumicene® M 3410 EP (EU) | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Andur 2-92 AP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Lupox® LW5300M | LG Chem Ltd. | PC+PBT | Lupox® |