Braskem PP H 605
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Z4rWs_Braskem-PP-H-605.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: H 605 is a low melt flow rate homopolymer with high transparency. This resin is designed for extrusion and thermoforming. H 605 exhibits excellent processability and high output, excellent stiffness/impact strength balance, high melt strength, outstanding optical properties and low odor/taste transfer. Applications: High transparency thermoformed packaging for food, cosmetic, health care and cleaning products; Flat and corrugated sheets for school and office folders |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 101 | ASTM D785 | |
| R-Scale | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 37.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 11 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1600 | MPa | ASTM D790 |
| Injection Molded | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, Injection Molded | 45 | J/m | ASTM D256 |
| 23°C, Injection Molded | 3.2 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 106 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 106 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 57.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ISO 306/A, ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | |||
| Injection Molded | 23 | % | ISO 13468-1 |
| 1000 µm, Injection Molded | 30 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 125/2 GL | A. Schulman Europe | ABS | POLYMAN® |
| PROTEQ™ H15QM63 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| Evermore PUR SA-2020MP | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Fainplast PVC PM 7010/S | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hostacom M2 U01 | LyondellBasell Industries | PP Homopolymer | Hostacom |