HiFill® POM CO GB25
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Yk7wA_HiFill-POM-CO-GB25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® POM CO GB25 is an Acetal (POM) Copolymer product filled with 25% glass bead. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.8 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3380 | MPa | ASTM D790 |
| Flexural Strength | 81.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 141 | °C | |
| 1.8 MPa, Unannealed | 116 | °C | |
| Melting Temperature | 162 | °C | |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 177 to 193 | °C | |
| Middle Temperature | 188 to 210 | °C | |
| Front Temperature | 182 to 199 | °C | |
| Nozzle Temperature | 177 to 204 | °C | |
| Processing (Melt) Temp | 193 to 216 | °C | |
| Mold Temperature | 82.2 to 121 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 8623 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| Nypol® PA A3 TZ NTLA010 NR339 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Arnite® AV2 360 S | DSM Engineering Plastics | PET | Arnite® |
| Leona™ 14G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| OmniCarb™ PC09SM | OMNI Plastics, LLC | PC | OmniCarb™ |