NILENE® P3 K25VA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | NILENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4XBNgO_NILENE-P3-K25VA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer 25% glass fibers reinforced chemically coupled, low flow, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.75 - 0.95 | % | Internal method |
| Flow direction | 0.25 - 0.45 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.2 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4800 | MPa | ISO 178 |
| Flexural Stress 2 | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ISO 306/A50 |
| -- | 128 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 3(2.00 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 4(600°C) | 25 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | US FMVSS302 |
| 4 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7751 T GF 15 GL | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| TOLEN H034 FF | SIBUR, LLC | PP Homopolymer | TOLEN |
| NEFTEKHIM PE 4252J (524F2) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| ExxonMobil™ PP7815E1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Flontech® FT-GL5-M5-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |