Sultron® 70G6-WR
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | Sultron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4WNFis_Sultron-70G6-WR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyphenylene Sulfide (Abbr. PPS) is a high performance thermoplastic polymer, offers excellent heat resistance, abrasion and radiation resistances, flame retardant, average mechanical properties, excellent dimensional stability and electrical properties. With all these outstanding properties, PPS compounded materials have already replace some of the metals as structural materials, and widely used in electronic and electrical, automotive, mechanical and chemical, aerospace, and military fields. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.40 | % | |
| Water Absorption (Saturation, 23°C) | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 145 | MPa | ISO 527-2/1270 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 11500 | MPa | ISO 178 |
| Flexural Stress 2 | 200 | MPa | ISO 178 |
| Coefficient of Friction | 0.20 | ISO 8295 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 26 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 250 | °C | ISO 75-2/A |
| CLTE - Flow (-20 to 150°C) | 2.5E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.40 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR1-5005F | Spartech Polycom | ABS | Spartech |
| TAISOX 7340M | Formosa Plastics Corporation | EVA | TAISOX |
| VALOX™ V2000DM resin | SABIC Innovative Plastics | PBT | VALOX™ |
| Ebalta AH 110 / GL | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| LNP™ STAT-KON™ MD000ISC compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |