Order Products : sales@su-jiao.com
ACRYLITE® MD™ L40
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | ACRYLITE® MD™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4VWVeB_ACRYLITE-MD-L40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACRYLITE® MD™ L40 acrylic polymer is an amorphous thermoplastic molding compound based on polymethyl methacrylate (PMMA) for the medical diagnostic industry. Typical properties of ACRYLITE® MD™ acrylic polymers are:
The special properties of ACRYLITE® MD™ L40 polymer are:
Application: Used for injection molded thin-wall medical devices requiring UV spectroscopy for fluid evaluation. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 26 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (Equilibrium) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ASTM D638 |
| Tensile Strength | 60.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.0 to 4.0 | % | |
| Break | 2.0 to 4.0 | % | |
| Flexural Modulus | 3030 | MPa | ASTM D790 |
| Flexural Strength | 97.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm) | 74.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 82.0 | °C | ASTM D1525 |
| CLTE - Flow (0 to 156°C) | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 92.0 | % | ASTM D1003 |
| Haze (3200 µm) | < 1.0 | % | ASTM D1003 |
| Yellowness Index (3.20 mm) | < 1.0 | YI | ASTM D1925 |
| UV Transmittance 1(3.20 mm) | > 88 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Wavelength: 340 nm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 3525 VP | Wacker Chemie AG | Silicone | POWERSIL® |
| Yanshan PE LD163 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| ACCUTECH™ CP0436M20CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Hifax 7430 XEP | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Lucky Enpla LPC1008F | Lucky Enpla Co LTD | PC | Lucky Enpla |