TAROLOX 111 G4 Y0
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4UsWgd_TAROLOX-111-G4-Y0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET medium viscosity 20% glass fibres reinforced, halogen free flame retardant UL94 V0, heat stabilized, good flow, good mechanical, thermal and electrical properties, low moisture absorption, good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.50 to 0.80 | % | |
| Flow | 0.30 to 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Granule Humidity 1 | < 0.030 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 8100 | MPa | ISO 178 |
| Flexural Stress 3 | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 36 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 50 | J/m | |
| 23°C | 65 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 228 | °C | ISO 75-2/A |
| Continuous Use Temperature | 150 | °C | IEC 60216 |
| Vicat Softening Temperature | 235 | °C | ISO 306/B50 |
| Ball Pressure Test (245°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 256 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 3.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 100 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 3224D | Formosa Plastics Corporation | LLDPE | TAISOX |
| Alkatuff® 601 | Qenos Pty Ltd | LLDPE | Alkatuff® |
| Dural 202/3 CLEAR 0003 | AlphaGary | PVC, Rigid | Dural |
| LNP™ THERMOCOMP™ WF007 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ RF0039S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |