Starex TX-0520HR
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4TZx3b_StarexTX0520HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex TX-0520HR is a methyl methacrylate/ABS (MABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical appliances. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.40 - 0.80 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.40 - 0.80 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.40 - 0.80 | % | ISO 2577 |
| Traffic : 3.20mm | 0.40 - 0.80 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 101 | ASTM D785 | |
| R scale | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1960 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 39.2 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 36.3 | MPa | ASTM D638 |
| Fracture | 35.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 25 | % | ASTM D638 |
| Fracture | 25 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 1860 | MPa | ASTM D790 |
| -- 6 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 53.9 | MPa | ASTM D790 |
| -- 8 | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 180 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 160 | J/m | ASTM D256 |
| 23°C 10 | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 86.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 to 3.0mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | |||
| 3200 µm | 2.0 | % | ASTM D1003 |
| 3200 µm | 2.0 | % | ISO 13468 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6594B-G80E-M | TSRC Corporation | SEBS | T-Blend® |
| TEREZ PA/PP 7500 GF 30 | TER HELL PLASTIC GMBH | Nylon 6+PP | TEREZ PA/PP |
| LUVOCOM® 1104-VAP 10 | Lehmann & Voss & Co. | PEK | LUVOCOM® |
| Petro Rabigh PE FS150A | Rabigh Refining & Petrochemical Co. | LLDPE | Petro Rabigh PE |
| Sylvin 7011EE-82FU Brown 7197 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |