Grivory® GVS-5H nat

Category:	Nylon 66+Nylon 6I/X , Polyamide 66 + PA 6I/X
Manufacturer:	EMS-GRIVORY
Trademark:	Grivory®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	4Srt95_Grivory-GVS-5H-nat.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Grivory® GVS-5H nat is a Polyamide 66 + PA 6I/X (Nylon 66+Nylon 6I/X) material filled with 50% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion or injection molding.

Important attributes of Grivory® GVS-5H nat are:

Flame Rated

RoHS Compliant

Good Aesthetics

Heat Stabilizer

Typical applications include:

Automotive

Appliances

Consumer Goods

Electrical/Electronic Applications

Engineering/Industrial Parts

General Information
Filler / Reinforcement	Glass Fiber, 50% Filler by Weight
Additive	Heat Stabilizer
Features	Aromatic Good Surface Finish Heat Stabilized
Uses	Appliance Components Automotive Applications Automotive Exterior Parts Automotive Interior Parts Consumer Applications Electrical/Electronic Applications Engineering Parts Household Goods Hydraulic Applications Industrial Applications Pneumatic Applications Power/Other Tools Sporting Goods
RoHS Compliance	RoHS Compliant
Appearance	Natural Color
Forms	Granules
Processing Method	Extrusion Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Tensile Modulus vs. Temperature (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.58	--	g/cm³	ISO 1183
Molding Shrinkage				ISO 294-4
Across Flow	0.50	--	%
Flow	0.10	--	%
Water Absorption				ISO 62
Saturation, 23°C	4.0	--	%
Equilibrium, 23°C, 50% RH	1.4	--	%

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	280	255	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	17000	16000	MPa	ISO 527-2
Tensile Stress (Break)	250	220	MPa	ISO 527-2
Tensile Strain (Break)	2.5	2.5	%	ISO 527-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	15	15	kJ/m²
23°C	15	15	kJ/m²
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	75	60	kJ/m²
23°C	90	80	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, Unannealed	240	--	°C	ISO 75-2/A
8.0 MPa, Unannealed	185	--	°C	ISO 75-2/C
Continuous Use Temperature				Internal Method
-- ¹	100 to 120	--	°C
-- ²	220	--	°C
Melting Temperature ³	260	--	°C	ISO 11357-3
CLTE				ISO 11359-2
Flow	1.5E-5	--	cm/cm/°C
Transverse	7.0E-5	--	cm/cm/°C

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	--	1.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+14	1.0E+14	ohms·cm	IEC 60093
Electric Strength	33	33	kV/mm	IEC 60243-1
Comparative Tracking Index	--	600	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flammability Classification (0.800 mm)	HB	--		IEC 60695-11-10, -20

Additional Information	Dry	Conditioned		Test Method
ISO Type	PA66 + PA6I/X, MH, 14-190, GF50	--		ISO 1874

Note Message
1 .	Long Term
2 .	Short Term
3 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Matrixx 14A4150	The Matrixx Group, Inc.	PP, Unspecified	Matrixx
RTP 205 A TFE 5	RTP Company	Nylon 6	RTP
Styropor® F 495 E	BASF Corporation	PS (EPS)	Styropor®
MAJORIS EC380	AD majoris	PP, Unspecified	MAJORIS
Pinnacle PP 3220	Pinnacle Polymers	PP Impact Copolymer	Pinnacle PP