Amilan® CM3211G35UB1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4RQ1ew_Amilan-CM3211G35UB1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM3211G35UB1 is a Polyamide 66 (Nylon 66) product filled with 35% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.50 to 0.80 | % | |
| Flow : 3.00 mm 2 | 0.20 to 0.40 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.40 | % | ASTM D570, ISO 62 |
| Saturation, 23°C | 3.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale, 23°C | 93 | ||
| R-Scale, 23°C | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| -40°C | 280 | MPa | |
| 23°C | 195 | MPa | |
| 80°C | 120 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Break, -40°C | 3.0 | % | |
| Break, 23°C | 3.0 | % | |
| Break, 80°C | 5.0 | % | |
| Flexural Modulus | ISO 178 | ||
| -40°C | 11000 | MPa | |
| 23°C | 9500 | MPa | |
| 80°C | 4800 | MPa | |
| Flexural Stress | ISO 178 | ||
| -40°C | 370 | MPa | |
| 23°C | 290 | MPa | |
| 80°C | 160 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 10 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 89 | kJ/m² | |
| 23°C | 95 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 228 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | °C | ISO 75-2/A |
| Melting Temperature | 265 | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.42 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+5 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIZ7008A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sylvin 2990-55 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| XYFLUOR® 860 | Greene, Tweed & Co. | Fluorelastomer | XYFLUOR® |
| ACCUCOMP™ CP0404L | ACLO Compounders Inc. | PP Copolymer | ACCUCOMP™ |
| Generic EVA | Generic | EVA | Generic |