Lotader® TX 8030

Category:	EEA , Ethylene Ethyl Acrylate Copolymer
Manufacturer:	Arkema
Trademark:	Lotader®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	4PvAFM_Lotader-TX-8030.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LOTADER® TX8030 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.

LOTADER® TX8030 is a versatile adhesive for extrusion coating or lamination, designed as:

Concentrate to be used in dry blend with LDPE. LOTADER® TX8030 improves adhesion of LDPE on aluminium foils, metallized or primerized films.

Ready for use resin to be used pure. LOTADER® TX8030 gives excellent adhesion on substrates likes aluminium foil, metallized plastics, paper, board, PE and its copolymers.

Coextrusion tie layer for PE/PA in extrusion coating process.

General Information
Features	Good Adhesion Good Drawdown Good Thermal Stability High Melt Stability Terpolymer
Uses	Adhesives Coating Applications Laminates Tie-Layer
Forms	Pellets
Processing Method	Coextrusion Extrusion Coating Laminating

Physical	Nominal Value	Unit	Test Method
Density	0.940	g/cm³	ISO 1183, ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	3.0	g/10 min	ASTM D1238, ISO 1133
Ethyl Acrylate Content	13.0	wt%
Maleic Anhydride Content	2.8	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	36		ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, Compression Molded)	12.0	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	700	%	ASTM D638, ISO 527-2
Flexural Modulus (Compression Molded)	130	MPa	ASTM D790, ISO 178

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	65.0	°C	ISO 306/A, ASTM D1525 ¹
Melting Temperature	95.0	°C	ISO 11357-3

Note Message
1 .	Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
TECHNYL® C R 218 V33 BLACK 21 N	Solvay Engineering Plastics	Nylon 6	TECHNYL® C
TRIMID® N6-TG30L-BK	Polymer Technology and Services, LLC	Nylon 6	TRIMID®
Ghaed ABS ABS-60	Ghaed Basir Petrochemicals Co.	ABS	Ghaed ABS
Softell TKG 300N 1 D62819	LyondellBasell Industries	PP Copolymer	Softell
LNP™ THERMOCOMP™ WF008 compound	SABIC Innovative Plastics	PBT	LNP™ THERMOCOMP™