DESLEN™ DSC501M6
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4P9l36_DESLEN-DSC501M6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLEN™ DSC501M6 is Polypropylene Mineral Filler 30% reinforced resin. It has good rigidity and heat resistance. Applications: DESLEN™ DSC501M6 is applied to electronic & electrical parts and air cleaner case which request good moldability, mechanical property and dimensional property . |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 - 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 34.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 3730 | MPa | ASTM D790 |
| Flexural Strength | 57.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 143 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 95.0 | °C | ASTM D648 |
| Melting Temperature | 163 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 200 - 220 | °C | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PP PPU 1080 | Qenos Pty Ltd | PP Homopolymer | Qenos PP |
| Moplen HP528NH | PolyMirae | PP Homopolymer | Moplen |
| Crastin® T841FR NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Exceed™ 2718CB | ExxonMobil Chemical | mPE | Exceed™ |
| Hostacom M2 N42 L356015 | LyondellBasell Industries | PP Homopolymer | Hostacom |