Latan 3 E71
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4OlchS_Latan-3-E71.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyoximethylene (POM). Toughened. High viscosity. Very high toughness properties and impact resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 2.4 to 2.8 | % | |
| Flow : 2.00 mm | 2.3 to 2.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 1900 | MPa | |
| 60°C | 1100 | MPa | |
| 90°C | 650 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 35.0 | MPa | |
| Yield, 60°C | 25.0 | MPa | |
| Yield, 90°C | 15.0 | MPa | |
| Break, 23°C | 35.0 | MPa | |
| Tensile Strain (Break, 23°C) | 120 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 190 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 70.0 | °C | |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 175 to 200 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 118NJ | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| NORYL™ WCA901 resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |
| DAI-EL™ G-717 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| DuraFlex 202-9 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraFlex |
| Karina CLEAR PVC COMPOUND -E 70/217-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |