Next PPS PPSG40-02BK
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4NhC3p_Next-PPS-PPSG40-02BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Polyphenylene Sulfide Glass Fiber Reinforced Black Compound Product Applications This is High performance material & This grade is used for Appliance, Automotive, Electric/Electronics, industrial Application Benefits Better dimensional stability, High thermal stability, chemical resistance & flame resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.25 | % | |
| Across Flow | 0.22 | % | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.040 | % | |
| Saturation 1 | 4.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 100 | ||
| R-Scale | 115 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8100 | MPa | ASTM D638 |
| Tensile Strength | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 6800 | MPa | ASTM D790 |
| Flexural Strength | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 275 | °C | |
| 1.8 MPa, Unannealed | 260 | °C | |
| Melting Temperature | 280 | °C | ASTM D2117 |
| RTI Elec | 240 | °C | UL 746 |
| RTI Imp | 220 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 26 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 130 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 290 to 300 | °C | |
| Middle Temperature | 310 to 320 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Mold Temperature | 130 to 145 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 387 TFE 10 | RTP Company | PC | RTP |
| XANTAR® MX 1002 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Petlon Prime B1-G15-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |
| Sumiliteresin® ECP-147 | SBHPP | Epoxy | Sumiliteresin® |
| VALOX™ ENH4550 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |