CALIBRE™ 2060-6
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4MqgGQ_CALIBRE-2060-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 2060-6 Polycarbonate resin is used in medical applications involving steam or ethylene oxide sterilization - though suitability for use in these applications is dependent upon autoclave cycle times and temperatures. CALIBRE 2060-6 provides exceptional clarity, heat resistance, impact strength, and processability, and has low contamination levels. The CALIBRE 2000 series of resins have been evaluated by certain biocompatibility tests based on on ISO 10993-1 (Biological Evaluation of Medical Devices) and are suitable for use in approved medical applications. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2410 | MPa | ASTM D638 |
| -- | 2410 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 72.4 | MPa | ASTM D638 |
| Break | 72.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2410 | MPa | ASTM D790 |
| -- 6 | 2410 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 96.5 | MPa | ASTM D790 |
| -- 8 | 96.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 910 | J/m | ASTM D256A |
| 23°C | 88 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 9(23°C) | 90.4 | J | ASTM D3763 |
| Tensile Impact Strength | 588 | kJ/m² | ASTM D1822 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | Method I (3 point load), 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Method I (3 point load), 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 3.39 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1800 A UV | RTP Company | PC+Acrylic | RTP |
| SHIN-A SEV-1131M80 | SHIN-A T&C | Epoxy | SHIN-A |
| TRANSMARE® BIO 35LA-0.001 | Transmare Compounding B.V. | PLA | TRANSMARE® BIO |
| Karina BLACK PVC COMPOUND -E 851-48/ 1-F-ISM (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom PPU X9057HS C11354 | LyondellBasell Industries | PP Copolymer | Hostacom |