LNP™ THERMOCOMP™ UF009S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4MULk5_LNP-THERMOCOMP-UF009S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* UF009S is a compound based on Polyphthalamide resin containing 45% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-1009 HS Product reorder name: UF009S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.65 | g/cm³ | ASTM D792 |
| -- | 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.46 | % | ISO 294-4 |
| Flow : 24 hr | 0.18 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.37 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 20400 | MPa | ASTM D638 |
| -- | 22700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 242 | MPa | ASTM D638 |
| Break | 253 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.7 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 18800 | MPa | ASTM D790 |
| -- | 18300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 392 | MPa | ASTM D790 |
| -- | 386 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 2 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 3 | 83 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.6 | J | ASTM D3763 |
| -- | 4.37 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 258 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ NF920 | Asahi Kasei Chemicals Corporation | ACS | Stylac™ |
| Dryflex® A1 600301 | ELASTO | SEBS | Dryflex® |
| Gebalon PC ULtimate G15 FR(y) | geba Kunststoffcompounds GmbH | PC | Gebalon |
| HiFill® PP GF20 CC LE | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| LNP™ COLORCOMP™ DX06407H compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |