TES J-4/30/VO
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | TES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Km4N2_TES-J-4-30-VO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Molding Parameters: The dry temperature at 16 hours is 165°F. For 2-zone machines, the rear temperature is 510-540°F, and the front temperature is 500-530°F. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6890 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 131 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8620 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 254 to 271 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Nozzle Temperature | 249 to 288 | °C | |
| Processing (Melt) Temp | 249 to 277 | °C | |
| Mold Temperature | 60.0 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 2500-4 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| APEX® 3301-55NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Gallonprene® GP520-5003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Formolene® 6507N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Eraclene® MS 80 U | Versalis S.p.A. | HDPE | Eraclene® |