LEXAN™ BY2710X resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4IrtzV_LEXAN-BY2710X-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BY2710X is a modified Polycarbonate (PC) resin. It is a non-filled, injection moldable grade with UL-94 V0 rating and is available in various opaque color options. |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2220 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 61.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 100 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2070 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 740 | J/m | |
| 23°C | 800 | J/m | |
| Instrumented Dart Impact (23°C, Total Energy) | 72.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 139 | °C | ASTM D1525 6 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 217 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Nozzle Temperature | 288 to 310 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 71.0 to 93.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® Electro 1700 | Momentive Performance Materials Inc. | Rubber | Silopren® |
| TRIBIT® 1551GN30 | Samyang Corporation | PBT | TRIBIT® |
| Bergadur™ PB40 G20 NC012 | PolyOne Corporation | PBT | Bergadur™ |
| Colorite Rigid PVC 1127A-012 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Plasmer 1045NM/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |