Panlite庐 G-3320M
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4IgMT4_Panlite-G-3320M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fiber reinforced grades-20% Glass fiber, Isotropy grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.40 to 0.60 | % | |
| Flow : 4.00 mm | 0.40 to 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3250 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 30 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3200 | MPa | ISO 178 |
| Flexural Stress 2 | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 60 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 137 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 127 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 141 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C | |
| RTI Elec (1.50 mm) | 130 | °C | UL 746 |
| RTI Imp (1.50 mm) | 125 | °C | UL 746 |
| RTI Str (1.50 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength 3 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.40 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | short time test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH301G6NT | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| Zytel® RS LC2600 BK043A | DuPont Performance Polymers | Nylon, Unspecified | Zytel® RS |
| BESTPOLUX PCBM/01 | Triesa Plastics | PC+PBT | BESTPOLUX |
| HAIPLEN EP50 T2 X2 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Karina IVORY PVC COMPOUND 90850-35/ 1-AY-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |