LNP™ THERMOCOMP™ DF002ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Icz2B_LNPTHERMOCOMPDF002ERcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF002ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features include Easy Molding, Mold Release. Also known as: LNP* THERMOCOMP* Compound DF-1002 EM MR Product reorder name: DF002ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 3.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3800 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 143 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 137 | °C | ISO 75-2/Af |
| CLTE - Flow (23 to 60°C) | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-1 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | IEC 60695-2-12 |
| 1.60 mm | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AESNO P20 TL | Arkema | Nylon 12 | Rilsan® |
| Mirathane™ S895 | Miracll Chemicals Co., Ltd. | TPU-Polyether | Mirathane™ |
| Telcar® TL-1050-80 | Teknor Apex Company | TPE | Telcar® |
| Celcon® GC25T | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| KumhoSunny PBT/ABS HAB8740 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |