LNP™ THERMOCOMP™ RF008 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4I6zxw_LNPTHERMOCOMPRF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF-1008 is a compound based on Nylon 66 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound RF-1008 Product reorder name: RF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.50 | g/cm³ | ASTM D792 |
| -- | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 - 3.0 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.66 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13900 | MPa | ASTM D638 |
| -- | 14100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 230 | MPa | ASTM D638 |
| Yield | 232 | MPa | ISO 527-2/5 |
| Fracture 3 | 210 | MPa | ASTM D638 |
| Fracture | 232 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.8 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/5 |
| Fracture 5 | 2.9 | % | ASTM D638 |
| Fracture | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 12400 | MPa | ASTM D790 |
| -- 7 | 11200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 229 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 338 | MPa | ASTM D790 |
| Fracture, 50.0mm span 9 | 337 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 10 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 11 | 86 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 18.0 | J | ASTM D3763 |
| -- | 4.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 260 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 12 | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 253 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 244 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 6.2E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 331 D FR | RTP Company | PC | RTP |
| RTP 103 CC | RTP Company | PP, Unspecified | RTP |
| Boltaron 2056 | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| ENVIROPLAS® ENV12-NC120 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| LNP™ LUBRICOMP™ RA004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |