LNP™ THERMOCOMP™ MX00709 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4HNqmM_LNP-THERMOCOMP-MX00709-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MX00709 is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this grade are: Heat Stabilized, UV Stabilized. Also known as: LNP* THERMOCOMP* Compound MF-1004 HS UV HP Product reorder name: MX00709 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7860 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 76.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.7 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 6180 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 123 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 151 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 F | RTP Company | Nylon 12 | RTP |
| Ratron® 250C6-WR | Asia International Enterprise (Hong Kong) Limited | PESU | Ratron® |
| Menzolit® BMC 0180 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| WELLAMID Nylon 6000 GV 25 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| SABIC® PPcompound 7700 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |