Order Products : sales@su-jiao.com
Sarlink® TPE EE-1250N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4H1N4Y_Sarlink-TPE-EE-1250N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE EE-1250N is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: extrusion. Sarlink®The typical application field of TPE EE-1250N is: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 53 | ISO 868 | |
| Shaw A, 15 seconds | 50 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Transverse flow : 100% strain | 1.17 | MPa | ISO 37 |
| Flow : 100% strain | 1.76 | MPa | ISO 37 |
| Tensile Strength | ISO 37 | ||
| Transverse flow : Fracture | 6.86 | MPa | ISO 37 |
| Flow : Fracture | 4.52 | MPa | ISO 37 |
| Tensile Elongation | ISO 37 | ||
| Transverse flow : Fracture | 870 | % | ISO 37 |
| Flow : Fracture | 690 | % | ISO 37 |
| Tear Strength - Across Flow | 24.9 | kN/m | ISO 34 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 15 | % | ISO 815 |
| 70°C, 22 hr | 30 | % | ISO 815 |
| 125°C, 70 hr | 76 | % | ISO 815 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 200 sec^-1) | 210 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MEGOLON™ S642 | AlphaGary | TP, Unspecified | MEGOLON™ |
| VINIKA® CE70TE | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Beta (ß)-PPR™ RA7050 | Borealis AG | PP Random Copolymer | Beta (ß)-PPR™ |
| Carbo-Rite™ F-1260 | Lubrizol Advanced Materials, Inc. | Acetal (POM) Copolymer | Carbo-Rite™ |
| Hypro® PP-CP 50/2 | Entec Polymers | PP Copolymer | Hypro® |
