ULTEM 4000 resin is an amorphous, opaque, glass fiber and polytetrafluorethylene (PTFE) reinforced polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217°C. This inherently flame retardant resin has UL94 V0 listing and is RoHs compliant. ULTEMTM 4000 resin is wear resistant and offers a reduced coefficient of friction. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.10 - 0.30 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.70 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| K (wear) Factor | Internal method | ||
| -- 2 | 380 | Internal method | |
| -- 3 | 12.0 | Internal method | |
| PV Limit 4 | 2.3 | MPa·m/s | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 140 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus 5 | 7000 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 30.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 8.0 | kJ/m² | ISO 179/2C |
| 23°C | 8.0 | kJ/m² | ISO 179/2C |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | 15 | kJ/m² | ISO 180/1U |
| 23°C | 15 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 100 mm span | 210 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 205 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 225 | °C | ISO 306/A50 |
| -- | 215 | °C | ISO 306/B50 |
| -- | 220 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.43 | W/m/K | ISO 8302 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 6.80 | IEC 60250 | |
| 60 Hz | 6.80 | IEC 60250 | |
| 1 MHz | 6.20 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.013 | IEC 60250 | |
| 60 Hz | 0.013 | IEC 60250 | |
| 1 MHz | 0.022 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 200 | V | IEC 60112 |
| Solution B | 100 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.840 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 48 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 350 - 395 | °C | |
| Middle Temperature | 360 - 405 | °C | |
| Front Temperature | 370 - 415 | °C | |
| Nozzle Temperature | 360 - 405 | °C | |
| Processing (Melt) Temp | 370 - 415 | °C | |
| Mold Temperature | 140 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | xE-10, PV=2000 psi-fpm vs Self |
| 3 . | xE-10, PV=2000 psi-fpm vs Steel |
| 4 . | 0.51 m/s |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 4223T (23407) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| NYCOA Polyamide 7551 T | Nycoa (Nylon Corporation of America) | Nylon 12 | NYCOA Polyamide |
| Tunhe PBS TH803S | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBS | Tunhe PBS |
| Neoflex™ 8140 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |
| SQUARE® LIM3900-60A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |