ESTOPLAST ZK 6002WW95
| Category: | PC , Polycarbonate |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | ESTOPLAST ZK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4GmA0e_ESTOPLASTZK6002WW95.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polycarbonate - Unfilled Grade, White Electrical & Electronic: Switches and Light Shielding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 24 | g/10 min | ASTM D1238 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 50 | % | ASTM D638 |
| Flexural Modulus | 2400 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 550 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 140 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 130 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 265 - 275 | °C | |
| Middle Temperature | 285 - 295 | °C | |
| Nozzle Temperature | 280 - 290 | °C | |
| Processing (Melt) Temp | 280 - 290 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Verolloy A1500 | PlastxWorld Inc. | ABS+Nylon | Verolloy |
| NEFTEKHIM PE 5122Q | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| Indothene HD 52GB010 | Reliance Industries Limited | HDPE | Indothene HD |
| Karina IVORY PVC COMPOUND - E-90901-35/ 1-D-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KMI PP KM-699IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |