MARPOL® LL6F 809-HSB
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4FOmXn_MARPOL-LL6F-809-HSB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: MARPOL® LL6F 809-HSB is a hexene LLDPE resin designed for blown film applications requiring high strength for maximum downgauging potential. Recommended Applications: General packaging, trash bags, ice bags, and trash can liners. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 165 | MPa | |
| 1% Secant, TD | 179 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 7.58 | MPa | |
| TD : Yield | 8.27 | MPa | |
| MD : Break | 53.1 | MPa | |
| TD : Break | 41.4 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 600 | % | |
| TD : Break | 600 | % | |
| Dart Drop Impact | 580 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 420 | g | |
| TD | 610 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 35 | ASTM D2457 | |
| Haze | 25 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPOA7400 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| Aplax P2515CN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| apilon 52bio® TB 40 | API SpA | TPU-Polyether | apilon 52bio® |
| Forprene® 6NE001A70 | SO.F.TER. SPA | TPV | Forprene® |
| LG PMMA IF870S | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |