Spartech Polycom SC1-1230
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4EVF30_Spartech-Polycom-SC1-1230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SC1-1230 is a medium viscosity ABS resin for injection molding that features 30% glass fiber reinforcement. It is heat stabilized and lubricated for good processing characteristics, and it exhibits good impact and chemical resistance. With the addition of the glass, this grade has increased strength and modulus properties. With the benefit of low moisture absorption, ABS can be used in a variety of environments. Being a very versatile product, SC1-1230 can be used for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 2.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 72.4 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 5550 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 107 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 99.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Melt Flow Rate, ASTM D1238: 1-4 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 210 - 240 | °C | |
| Middle Temperature | 215 - 245 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Nozzle Temperature | 218 - 260 | °C | |
| Processing (Melt) Temp | 218 - 260 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F02-139A | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Network Polymers PP PPB 25 0216 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Chiao Fu PA66 MD212G33 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| KOCETAL® UR302LO | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Karina CLEAR PVC COMPOUND 75/204-D-AT-IS-H (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |