Duratuf™ 903U2/X
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Duratuf™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4E1asY_Duratuf-903U2-X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Duratuf™903U2/X is a polyoxymethylene (POM) homopolymer material,. This product is available in North America and is processed by injection molding. Duratuf™The main features of 903U2/X are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 75 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2790 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 163 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.3 | °C | ASTM D648 |
| Melting Temperature | 178 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Tensile Elongation, ASTM D638: >75% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 210 - 221 | °C | |
| Mold Temperature | 79.4 - 98.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 6.35 - 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Nylon 1013 NW8 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| Nylfor® A2 E6/2A NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Hylex® P1017G30HB | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Karina BEIGE PVC COMPOUND -E 828-08/497-Y-RT | Karina Ind. e Com. de Pl谩sticos Ltda | PVC, Unspecified | Karina |
| LONGLITE® LCP LCP-270 N3G | CCP Group | LCP | LONGLITE® LCP |