Geon™ Vinyl Flexible A8500
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Flexible |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Cm57l_Geon-Vinyl-Flexible-A8500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Interior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 to 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 85 | ||
| Shore A, 15 sec | 75 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Break | 16.5 | MPa | |
| 100% Strain | 9.65 | MPa | |
| Tensile Elongation 2(Break) | 350 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3 | 77.1 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 45 | % | ASTM D395 |
| Clash-Berg Modulus (-20°C) | 310 | MPa | ASTM D1043 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -32.8 | °C | ASTM D746 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 4(1910 µm) | 80.0 | % | ASTM D1003 |
| Haze (1910 µm) | 5.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 193 to 204 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 174 to 179 | °C |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | Die C, 510 mm/min |
| 4 . | CIE Illuminant C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209 K FR | RTP Company | PARA | RTP |
| RTP 106CC SP | RTP Company | PP Homopolymer | RTP |
| Dynaglide® DW 602 | DeWAL Industries | PTFE | Dynaglide® |
| LNP™ THERMOCOMP™ 5C004 compound | SABIC Innovative Plastics | PVDF | LNP™ THERMOCOMP™ |
| LUVOCOM® 1105-1330 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |